Peg height of near-field transducers

ABSTRACT

A method is provided for characterizing the peg region of a near-field transducer incorporated into a write head of a HAMR magnetic recorder. The method includes providing excitation radiation to one or more near-field transducers. The near-field transducers include an enlarged disk region and a peg region at least partially in contact with the enlarged disk region. The method further includes filtering output radiation from the near-field transducers by passing a portion of photoluminescent radiation emitted by the near-field transducers in response to the excitation radiation and substantially blocking the excitation radiation transmitted by the near-field transducers. The method also includes detecting the portion of photoluminescent radiation and characterizing the peg region of at least one of the plurality of near-field transducers.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. Ser. No. 14/016,441, filed Sep.3, 2013, which is incorporated herein by reference in its entirety.

SUMMARY

Some embodiments include a method for characterizing a peg region of anear-field transducer with regard to peg height. Excitation radiation isemitted from an excitation light source through an optical input couplerto a plurality of near-field transducers (NFTs). The NFTs include anenlarged region and a peg region at least partially in contact with theenlarged region. The output radiation from the NFTs is filtered using ashort wavelength pass optical filter. Filtering involves passing aportion of photoluminescent radiation emitted by the NFTs in response tothe excitation radiation and substantially blocking the excitationradiation. The portion of photoluminescent radiation emitted by the NFTsis detected and an electrical signal is generated in response todetection of the photoluminescent radiation. The peg region of an NFT ischaracterized based on the electrical signal. Characterization of thepeg region can include determining peg height, determining if the pegheight meets a predetermined height and/or determining if the peg heightprovides an acceptable NFT response. In some embodiments, the pluralityof NFTs is part of a wafer bar that includes at least two NFTs that havedifferent peg heights.

Some embodiments are directed to a system that includes an excitationlight source configured to provide excitation radiation to a wafer barthat contains a plurality of NFTs. The NFTs have an enlarged region anda peg region having a peg height. The peg region is at least partiallyin contact with the enlarged region. The plurality of NFTs includes NFTshaving at least two different peg heights. An optical filter isconfigured to substantially pass a portion of photoluminescent radiationemitted by the enlarged region in response to the excitation radiationand to substantially block the excitation radiation. A detector isconfigured to detect the portion of photoluminescent radiation and tooutput an electrical signal in response to detection of the portion ofphotoluminescent radiation.

Other embodiments are directed to a write head for heat-assistedmagnetic recording that includes a near-field transducer. The near-fieldtransducer has an enlarged region and a peg region that is at leastpartially in contact with the enlarged region. The peg region of thenear-field transducer has a peg height for recording of from about 15 nmto about 30 nm. In some embodiments, the peg height is about 20 nm.

In another embodiment, a system for heat-assisted magnetic recording isdisclosed that includes a recording medium and a near-field transducerthat is capable of focusing energy on at least a portion of therecording medium. The near-field transducer includes an enlarged regionand a peg region at least partially in contact with the enlarged region.The peg region has a peg height of from about 10 nm to about 20 nm forrecording. In some embodiments, the peg height is about 15 nm.

The above summary is not intended to describe each disclosed embodimentor every implementation of the present disclosure. The drawings and thedetailed description below more particularly exemplify illustrativeembodiments

BRIEF DESCRIPTION OF THE DRAWINGS

Throughout the specification reference is made to the appended drawings,where like reference numerals designate like elements, and wherein:

FIG. 1 shows a process flow diagram that illustrates a high-levelsummary of a portion of a process for fabricating a slider that mayinclude a near-field transducer (NFT) characterization step according tothe approaches discussed herein.

FIGS. 2, 3, 4A, and 4B provide cross-sectional diagrams that illustratevarious NFT subassemblies for which the peg height of a NFT can becharacterized using the approaches discussed herein.

FIG. 5 depicts a characterization subassembly that may be used todetermine the peg height in accordance with some embodiments.

FIG. 6A provides an example spectral characteristic of the excitationradiation for the systems of FIG. 3.

FIG. 6B provides an example spectral characteristic of photoluminescentradiation emitted by an NFT in response to the excitation radiation.

FIG. 6C illustrates shortwave pass filtered radiation that is used tocharacterize the NFT under test in accordance with various embodiments.

FIG. 7 is a block diagram of a characterization system according tovarious embodiments.

FIG. 8 shows a possible spectral characteristic for the shortwave passfilter used in the system of FIG. 7.

FIG. 9 shows a possible spectral characteristic of a suitable dichroicbeam splitter used in the system of FIG. 7.

FIG. 10 is a graph based upon modeling showing the relationship betweenCE₅₀ (light absorption in a medium of a 50 nm×50 nm footprint) and pegheight in nm.

FIG. 11 shows a modeled response of the integrated electric field, E,over the near-field transducer as a function of peg height, in nm,measured from the break point where the peg meets the edge of theenlarged disk region and the tip of the peg.

FIG. 12 is a plot of recording performance (measured in signal-to-noiseratio) as a function of calculated NFT overlap (related to peg height)for various lots of wafer bars containing NFTs with different pegheights.

FIG. 13 is graph of two-photon photoluminescence (TPPL) signal (nA) as afunction of calculated NFT overlap for various lots of wafer barscontaining NFTs with different peg heights.

FIG. 14 is a plot of TPPL current (nA) vs. peg height (nm) for embodiedNFTs.

FIG. 15 is a transmission electron micrograph (TEM) of one of theembodied NFTs.

FIG. 16 is a flow diagram of a method of characterizing the peg regionof an NFT.

FIG. 17 is a flow diagram of identifying a peg height that providesacceptable NFT performance and using the identified peg height tofabricate NFTs.

The figures are not necessarily to scale. Like numbers used in thefigures refer to like components. However, it will be understood thatthe use of a number to refer to a component in a given figure is notintended to limit the component in another figure labeled with the samenumber.

DETAILED DESCRIPTION

In the following description, reference is made to the accompanying setof drawings that form a part of the description hereof and in which areshown by way of illustration several specific embodiments. It is to beunderstood that other embodiments are contemplated and may be madewithout departing from the scope of the present disclosure. Thefollowing detailed description, therefore, is not to be taken in alimiting sense.

Unless otherwise indicated, all numbers expressing feature sizes,amounts, and physical properties used in the specification and claimsare to be understood as being modified in all instances by the term“about.” Accordingly, unless indicated to the contrary, the numericalparameters set forth in the foregoing specification and attached claimsare approximations that can vary depending upon the desired propertiessought to be obtained by those skilled in the art utilizing theteachings disclosed herein. The use of numerical ranges by endpointsincludes all numbers within that range (e.g. 1 to 5 includes 1, 1.5, 2,2.75, 3, 3.80, 4, and 5) and any range within that range.

The present disclosure relates to methods and systems for determiningcritical dimensions of near-field transducers (NFTs) that can be used inapplications such as heat-assisted magnetic recording (HAMR). The NFTsinclude an enlarged region and a peg region at least partially incontact with the enlarged region. A HAMR device can utilize a magneticrecording media (e.g., hard disk) that can overcome superparamagneticeffects that limit the areal data density of typical magnetic media. Inorder to record on this media, a small portion of the media can belocally heated while being written to by a magnetic write head. Acoherent light source such as a laser, e.g., laser diode, can providethe energy to create hot spots, and optical components built into aslider that houses the write head can be configured to direct thisenergy onto the recording medium.

When applying light to a HAMR medium, light from the light source can beconcentrated into a small hotspot over the track where writing is takingplace. As a result of what is known as the diffraction limit, opticalcomponents cannot be used to focus light to a dimension that is lessthan about half the wavelength of the light. For example, the lasersused in some HAMR designs produce light with wavelengths on the order of800-900 nm, yet the desired hot spot can be on the order of 50 nm orless. Thus the desired hot spot size can be well below half thewavelength of the light, and, due to diffraction, optical focuserscannot be used to obtain the desired hot spot size. As a result, anoptical near-field transducer (NFT) can be employed to create thesesmall hotspots on the media.

The NFT is a near-field optics device designed to reach local surfaceplasmon conditions at a designed wavelength of incident light. ExampleNFT transducers may include a plasmonic optical antenna or a metallicaperture and a focusing element. The focusing element concentrates lighton the transducer region (e.g., at the focal region) near where theoptical antenna or a metallic aperture is located. Example focusingelements may include solid immersion lenses (SIL), solid immersionmirrors (SIM), and/or three-dimensional channel waveguide for lightdelivery to an NFT. The NFT is designed to achieve surface plasmonresonance in response to this concentration of light.

Surface plasmons are collective oscillations of surface charges that areconfined to an interface between a dielectric and a metal. When surfaceplasmons are resonantly excited by an external optical field, the fieldamplitude in the vicinity of the surface may be orders of magnitudegreater than that of the incident field. Moreover, the region ofenhanced field may be tightly confined to a spot much smaller than theincident wavelength. At resonance, a high electric field surrounds theNFT due to the collective oscillations of electrons at the metalsurface. Part of this field will tunnel into a storage medium and getabsorbed, thereby raising the temperature of a spot on the media as itbeing recorded.

The NFT may be located near an air bearing surface (ABS) of a sliderused for magnetic data storage, and may be placed in close proximity toa write head that is also part of the slider. This co-location of theNFT with the write head facilitates heating the hot spot during writeoperations. The focusing element, e.g., waveguide, and NFT may be formedas an integral part of the slider that houses the write head. Otheroptical elements, such as couplers, mirrors, prisms, etc., may also beformed integral to the slider. The optical elements used in HAMRrecording heads are generally referred to as integrated optics devices.

The field of integrated optics relates to the construction of opticsdevices on substrates, sometimes in combination with electroniccomponents, to produce functional systems or subsystems. For example, anintegrated optics device may be built up on a substrate using layerdeposition techniques. In reference now to FIG. 1, a process flowdiagram illustrates a high-level, short summary of a portion of aprocess for fabricating a slider that includes integrated opticsincluding an NFT and various optical coupling and/or light positioningelements. Block 102 represents a wafer-level stage. A wafer 104 isformed using semiconductor manufacturing processes (e.g., thin filmdeposition, chemical-mechanical polishing/planarization, etc.) and eachwafer 104 generally includes a plurality of sliders (e.g., slider 106)that are later cut into bars for further processing. Each slider 106includes an NFT subassembly comprising a waveguide focusing element andan NFT.

Block 112 represents an upstream stage where the wafer 104 has been cutinto bars 114. Each bar 114 includes a plurality of sliders that arebatch-processed. Stage 112 may involve attaching top bond pads (e.g.,part of a slider-gimbal electrical interface). Block 115 shows that insome processes the bars are cut in to a number of individual sliders 106a, 106 b prior to slider characterization.

Block 120 illustrates a characterization process for individual slider106 a. In some embodiments, the characterization process is performed atthe block level before the slider block 114 is cut into individualsliders. As discussed in more detail herein, some embodiments involvecharacterizing the peg region and/or determining if the peg height ofthe NFT is suitable for effective operation based on photoluminescentradiation from the NFT. The characterization process includes providingexcitation radiation from a light source 116, filtering the radiationemanating from the air bearing surface of the slider, and detecting thefiltered radiation using a detector 118. The NFT, including peg regioncan be characterized based on the filtered radiation detected by thedetector 118.

FIG. 2 provides a cross-sectional diagram that illustrates one exampleof a portion of a slider that includes NFT subassembly 200. The NFTsubassembly shown in FIG. 2 represents an end-fire arrangement. NFTsubassembly 200 may be incorporated into a slider and optical inputcoupler 209 of the NFT subassembly 200 may be aligned withlight-emitting device 290.

NFT subassembly 200 shown in FIG. 2 is fabricated in slider 205 andincludes optical input waveguide coupler 209, first mirror 211, secondmirror 212, solid immersion mirror (SIM) 202, and NFT optical antenna203. NFT subassemblies 200 that operate by end-fire technique as shownin FIG. 2 may be incorporated into each slider 106 of bar 114 shown inFIG. 1. NFT subassembly 200 illustrates one particular configuration,although it will be appreciated that many configurations of NFTsubassemblies are possible and can be characterized using the approachesdiscussed herein.

FIGS. 2-4B illustrate several sliders that include NFTs, wherein eachNFT has an enlarged portion and a peg portion. Each of these NFTs can becharacterized using the techniques disclosed herein. The operation ofthe NFTs is dependent in part on peg height. Thus, characterizationaccording to the approaches discussed herein can provide informationabout the peg height of the NFT. In some implementations, as part of theNFT characterization, peg heights of the NFTs can be determined and/orit can be determined if the pegs have a desired peg height. In someembodiments, characterization of the peg region includes determining ifthe peg height meets a predetermined height and/or provides apredetermined or desired NFT response.

In the example illustrated in FIG. 2, NFT subassembly 200 receives lightemitted from light source 290 via input waveguide coupler 209 which is athree-dimensional channel waveguide of finite width waveguide core. Innormal use, light source 290 may comprise an edge emitting or surfaceemitting laser diode, for example. The light emerging from waveguidecoupler 209 is directed in a solid immersion mirror (SIM), or planarsolid immersion mirror (PSIM) indicated by way of SIM sidewall 202 inFIG. 2, by first mirror 211 and second mirror 212. NFT 203 (alollipop-type NFT with a circular cross-section and peg) is located atthe focus point of SIM 202.

NFT 203 shown in FIG. 2 comprises a “lollipop” configuration thatcombines a circular enlarged disk region with a peg region, althoughother configurations, such as a square enlarged region such as thatillustrated in FIG. 3, may be used. The lollipop dimensions are selectedto function as an antenna for the incident light, to resonate at theexcitation wavelength, and to transfer energy into the peg and thus tothe medium via the feedgap at tip 203 a of NFT 203. The NFT is atransducer that can be made of any plasmonic material (e.g., Au, Ag, Cu,or ZrN) and may be positioned at or near the focal region of light 210.

Waveguide core 201 may be formed from any material that has a higherindex of refraction than cladding. For example, waveguide core 201 maybe made from Ta₂O₅, TiO₂, ZnS, or SiN. The PSIM 202 may be formed as aparabolic cutout of surrounding dielectric waveguide material (e.g.,Al₂O₃, SiO₂, SiO_(x)N_(y), MgO, HfO₂, Y₂O₃, Ta₂O₅, or TiO_(x)). Thecutout may be formed from/coated with a reflective material (e.g., Au,Al), so that light rays 210 entering PSIM 202 by way of waveguide core201 are focused to a focal region to strongly couple to NFT 203 andgenerate surface plasmons.

FIG. 3 shows another configuration for NFT subassembly 300 that may beincorporated into a slider. NFT subassembly 300 may be incorporated intoa slider and the optical input coupler 318 of NFT subassembly 300 may bealigned with light-emitting device 310. FIG. 3 shows light source 310positioned at mounting surface 327 of slider 362. In the configurationof FIG. 3, the light delivery path includes three mirrors, twodirectional mirrors 342, 344 and the SIM 345. NFT 347 is offset fromwaveguide input coupler 318 along the x axis by distance 346, e.g.,about 102 micrometers (μm). Light path 399 passes through waveguideinput coupler 318 to first reflecting mirror 342. Light reflected bymirror 342 encounters second reflecting mirror 344 which redirects light399 toward SIM 345 which focuses the light on the NFT 347.

FIG. 4A illustrates NFT subassembly 400 that has a straight throughlight path. NFT subassembly 400 may be incorporated into slider 420 andoptical input coupler 425 of NFT subassembly 400 may be aligned withlight-emitting device 410.

In this configuration, waveguide input coupler 425 couples light intolight delivery path 488 within slider 420. Light from light source 410is coupled into light delivery path 488 through optical input coupler425, which comprises a waveguide. Optical input coupler 425 carrieslight to SIM 460 which focuses the light onto NFT 450.

FIG. 4B illustrates NFT subassembly 405 that has a straight throughlight path and does not have a SIM. NFT subassembly 405 may beincorporated into slider 462 and optical input coupler 426 of NFTsubassembly 405 can be aligned with light-emitting device 410.

In this configuration, optical input coupler 426 couples light intolight delivery path 461 within slider 420. As shown in this example,optical input coupler 426 may be a waveguide that extends toward NFT 451and is configured to carry the light that couples in from light-emittingdevice 410 to NFT 451. In various configurations, waveguide 426 extendsat least a majority of the distance between slider surface 464 and airbearing surface (ABS) 463 and may extend the entire distance. FIG. 4Bshows waveguide 426 that extends the entire distance between surface 464and ABS 463. NFT 451 could be placed in a waveguide cladding layer,e.g., a cladding layer between the NFT and magnetic write pole, or NFT451 could be positioned within the waveguide 426 at or near the end ofwaveguide. A SIM is not included in the embodiment illustrated in FIG.4B.

Dark field microscopy has been attempted to characterize opticalantennas by measuring the light scattering from NFT, however thischaracterization technique may not be applicable in the presence of anincident beam (“bright field”) in actual devices. Dark field microscopymay also not be very sensitive to the peg height. The peg height of theNFT can influence the NFT recording performance. Characterization of theNFT by the thermo-reflectance pump/probe method, for example, measuresoptical changes due to absorption of the NFT, however, the pump/probemethod can suffer from variation due to the thermal environment. Somecharacterization methods are less sensitive to certain parameters thatare useful to track in a manufacturing environment.

According to some embodiments discussed herein, characterization of theNFT subassemblies may be accomplished by sensing filteredphotoluminescent radiation emitted by the NFT in response to high energyexcitation radiation. The photoluminescent radiation is stronglyenhanced by the local surface plasmons that are generated at the NFTsurface. The photoluminescent radiation generated in the NFT includeswavelengths shorter than the excitation radiation by two-photonexcitation. Two-photon luminescence is luminescence excited bytwo-photon absorption. Two-photon induced photoluminescence in noblemetals such as gold and silver is generally considered as a three-stepprocess. Electrons from occupied d bands are first excited by two-photonabsorption to unoccupied states of the sp-conduction band. Second,subsequent intra-band scattering processes move the electrons closer tothe Fermi level. Third, the relaxation of the electron-hole pairrecombines either through non-radiative processes or by emission ofluminescence. The emission of luminescence is proportional to E⁴, whereE denotes the electric-field amplitude. Local surface plasmons at thesurface of the NFT enhance the luminescence significantly.

In various configurations, the characterization system includesshortwave pass spectral filters, notch filters and/or beam splitterswith a wavelength edge that are used to separate the bright field light(e.g., the excitation light) from the photoluminescent light emanatingfrom the NFT.

An example subsystem for characterizing NFT subassemblies in accordancewith some embodiments is described with reference to FIGS. 5 and 6A-6C.Excitation light source 501 emits excitation radiation 503 that passesthrough focusing lens 505 and illuminates slider 511 comprising anoptical input coupler and an NFT. FIG. 6A provides an exemplary spectraldistribution of the focused excitation radiation 506 that is centered atwavelength λ_(E). The spectral distribution diagrams of FIGS. 6A-C areidealized as Gaussian distributions of arbitrary peak magnitudes,however, it will be appreciated that, in general, the distributions neednot be Gaussian. In response to excitation radiation 506, the NFT inslider 511 emits white light super-continuum photoluminescence 512 atthe feedgap and tip of the optical antenna (e.g., see, 203 a, FIG. 2). Aportion of excitation radiation 506 that is not absorbed in the NFT isalso transmitted through slider 511.

An exemplary spectral distribution of electromagnetic radiation 512emerging from the NFT of slider 511 that includes both aphotoluminescent radiation component 513 and excitation radiationcomponent 506 is shown in FIG. 6B. In this example, the photoluminescentradiation component 513 is shown as having an arbitrary peak or centralwavelength, λ_(L), and excitation radiation component 506 is shown ashaving an arbitrary peak or central wavelength, λ_(E). Although theidealized spectral distributions and magnitudes of FIGS. 6A-6C do notnecessarily correspond to actual spectral distributions and magnitudesof the photoluminescent and excitation radiation, FIG. 6C illustratesthat photoluminescent radiation 613 emitted by the NFT includes shorterwave radiation and/or has shorter peak or central wave when compared toexcitation radiation 606.

Radiation 512 that emerges from the NFT of slider 511 is collected andcollimated by lens 516 and passes through shortwave pass filter 520having cutoff wavelength, λ_(F). Shortwave pass filter 520 substantiallyremoves components of radiation 512 having a wave longer than λ_(F). Assuch, shortwave pass filter 520 substantially absorbs or blocksexcitation radiation component 506 and also absorbs or blocks thatportion of the photoluminescent radiation that has wavelength greaterthan λ_(F). The shortwave pass filter substantially passes wavelengthsof the photoluminescent radiation with wavelengths greater than λ_(F),including radiation 525 shown in FIG. 6C.

Returning now to FIG. 5, filtered radiation 525 impinges on detector530, such as a photomultiplier tube (PMT) or a solid statephotodetector. Photodetector 530 provides electrical signal output 535in response to incident filtered radiation 525 that can be used tomeasure the filtered photoluminescent radiation emitted by the NFT.

FIG. 7 shows an embodiment of a subsystem 700 suitable for use incharacterizing NFTs in accordance with some embodiments. As with thesystem of FIG. 5, the system of FIG. 7 also involves detectingphotoluminescent light emanating from the NFT in response to excitationradiation and filtering using a shortwave pass filter.

As shown in FIG. 7, high energy excitation radiation is provided bymode-locked femtosecond or picosecond laser 701, e.g., a Ti:sapphirelaser emitting 160 femto second pulses at a repetition rate of 76 MHzand having a wavelength of about 805 nm±10 nm. In some cases, it may bedesirable to reduce the intensity of the excitation light 786 that isincident on the NFT subassembly under test. In these cases, a beamsampler may be used to pass a portion of the excitation light to a beamdump. As illustrated in FIG. 7, the excitation light 786 emitted bylaser 701 reflects from optional Fresnel beam sampler 702. Portion 786 bof the excitation radiation is transmitted through Fresnel sampler 702to beam dump 703. Another portion 786 a of the excitation radiation isdirected toward optional beam expander 704 that expands the beam ofexcitation radiation 786 a emitted by the laser. In some cases, system700, optionally, includes subsystem 706 configured to monitor excitationradiation 786 a at the output of beam expander 704. Optional excitationradiation monitor 706, can include, for example, neutral, non-polarizingbeam splitter cube 706 a that splits off sample 786 c of excitationradiation 786 a and directs sample radiation 786 c to photodetector 706b. Photodetector 706 b generates signal 706 c in response to theincident sample radiation 786 c.

Excitation radiation 786 d passes through achromatic half-wavelengthwaveplate 707 that can rotate the polarization direction of radiation786 d to the desired direction for NFT excitation. Excitation radiation786 d is focused by focusing lens 708 onto the input waveguide coupler(or grating coupler) in subassembly 711 being tested. For example, asuitable lens for lens 708 is an aspherical lens that has a numericalaperture (NA) of about 0.25. In some test setups, NFT subassembly 711being tested is disposed on a bar that includes many NFT subassemblies.In response to excitation radiation 786 d, NFT subassembly 711 beingtested emits photoluminescent radiation and also a portion of theexcitation radiation is transmitted through NFT subassembly 711. Thus,radiation 787 emanating from NFT subassembly 711 is a combination of thephotoluminescent radiation and the excitation radiation, as previouslydiscussed.

Combined radiation 787 output from NFT subassembly 711 under test iscollimated and collected by lens 718 of high numerical aperture, e.g.,NA of about 0.90. To image the radiation exiting surface of NFTsubassembly 711, system 700 may include imaging subsystem 760. Theimaging subsystem includes fiber bundle white light source 720 thatprovides white light 721 for imaging NFT subassembly 711. White light721 is coupled into light beam 788 by broadband mirror 722. Arrow 725indicates that components of the imaging subsystem, e.g., white lightsource 720 and mirror 722 may be used for set up and then removed fromthe beam path. Radiation 788 includes excitation radiation transmittedthrough NFT subassembly 711, and includes photoluminescent radiationemitted by the NFT subassembly in response to the excitation radiation.In some configurations, imaging system 760 is used to position NFTsubassembly 711. In these configurations, white light 721 generated bywhite light source 720 will not be a component of radiation 788 when thephotoluminescence of NFT subassembly 711 is being measured.

Radiation 788 can be redirected through mirror 727 and through shortwavepass spectral filter 739. Shortwave pass filter 739 substantially blocks(absorbs) the excitation radiation and substantially passes a portion ofthe photoluminescent radiation emitted by the NFT. FIG. 8 shows apossible spectral characteristic for filter 739. A filter having thecharacteristics of FIG. 8 has an optical density of 10⁻⁷ and blockstransmission by a factor of about 10⁻⁷ or by about 10⁻⁴, for example, inthe wavelength range longer than the cut-off wavelength (which is 650 nmin FIG. 8), where the excitation radiation (e.g., 805 nm±10 nm) islocated. In contrast, the filter shown in FIG. 8 substantially passesradiation (has an optical density close to 0 or 100% transmission) inthe wavelength range from about 320 nm to about 650 nm. Arrow 731indicates that the filter 739 may be moved out of the radiation pathduring measurement of the transmitted excitation radiation.

After filter 739, a confocal detection scheme is used. Radiation 789that passes through filter 739 subsequently passes through non-coated orbroad-band coated plano-convex imaging lens 735 or a doublet. Irisdiaphragm or slit 740 is placed near the focal point of imaging lens 735to reduce the background noise. Radiation 790 that passes through theiris diaphragm or slit 740 is imaged by biconvex lens 745 and throughdichroic beam splitter 747. Dichroic beam splitter 747 has a 685 nm edgethat separates incoming radiation 791 into two spectrally distinctbeams. Any radiation with wavelength above the 685 nm edge istransmitted, whereas radiation with wavelength below the 685 nm edge isreflected. The spectral characteristic of a suitable dichroic beamsplitter is shown in FIG. 9. Incoming radiation 791 is separated bydichroic beam splitter 747 into first radiation beam 792 with wavelengthgreater than 685 nm and second radiation beam 793 with wavelength lessthan 685 nm. Shortwave pass filter 739 in combination with dichroic beamsplitter 747 reject the excitation radiation wavelengths from secondradiation beam 793 by a factor of about 10⁻⁷, or about 10⁻¹⁰ or evenabout 10⁻¹⁴.

First radiation beam 792 is directed to photodetector 750 configured tomeasure the excitation radiation transmitted through an NFT subassembly.Second radiation beam 793 comprises the components from thephotoluminescence from NFT under test 711 and light from the white lightsource 720 that was reflected by NFT bar 714. Optical element 755directs the photoluminescent radiation to both or either of PMT 770 andCCD 756. Optical element 755 is on a translation stage and may be a beamsplitter or moveable mirror. If optical element 755 is a moveablemirror, the moveable mirror directs the luminescence to PMT 770 or toCCD 756. If optical element 755 is a beam splitter, optical elementdirects the luminescence to both the PMT 770 and CCD 756. With the whitelight moved in the light path and without the presence of shortwave passfilter 739 in the light path, the light transmitted through a device,including the NFT radiation, and white light 794 reflected from a deviceis imaged onto a cooled charge coupled device (CCD) that is a part ofimaging subsystem 760; with the white light moved out of the light pathand shortwave pass filter 739 moved into the light path, the two-photoninduced photoluminence from NFT is either directed to PMT 770 or CCD 756if 755 is a mirror, or, is split into both PMT 770 and CCD 756 if 755 isa beam splitter. The photoluminescence image of slider 711 can be viewedusing the CCD without the presence of white light radiation and with thepresence of shortwave pass filter. White light source 720 is removedfrom the optical path to measure photoluminescence (imaging anddetection).

The photoluminescence 795 is detected by detector 770, e.g.,photomultiplier tube (PMT) or other type of detector. In response tophotoluminescence 795, detector 770 generates electrical signal 775 thatis based on the amount of radiation incident on detector 770. In somecases, the system may include unit 780 configured to facilitatediscerning a weak signal from a noisy background to enhance the signalto noise ratio of electrical signal 775. In some cases, the SNR isenhanced by amplifying electrical signal 775 using a lock-in amplifierthat is locked to the repetition frequency of the laser pulses. In someembodiments, unit 780 may employ a photo-counting technique that uses anappropriate threshold to trigger the photon counting ofphotoluminescence 795 by the detector 770.

The characterization subsystems illustrated in FIGS. 5 and 7 can be usedto characterize NFT performance, particularly with regard to peg height.Peg height (used interchangeably with peg length herein) of near-fieldtransducers is related to HAMR head recording performance as are otherparameters such as thermal gradient, thermal spot size, near-fieldtransducer efficiency, and head reliability. Peg heights that provideefficient NFT performance are related to the dimension and shape of thenear-field transducer, the surrounding dielectric material for thenear-field transducer, and the wavelength of excitation. FIG. 10 is agraph based upon modeling showing the relationship between CE₅₀ (lightabsorption in a medium of a 50 nm×50 nm footprint) and peg height in nm.The modeled near-field transducer had a peg thickness of 30 nm and anenlarged disk region having a diameter of 250 nm. When the excitationwavelength is 830 nm and the dielectric material surrounding thenear-field transducer is alumina, pegs having heights of between about17 nm and 28 nm absorbed a maximum amount of light energy when arecording media was present as shown in FIG. 10.

FIG. 11 shows a modeled response of the integrated electric field, E,over the near-field transducer as a function of peg height, in nm,measured from the break point where the peg meets the edge of theenlarged disk region and the tip of the peg. This response was obtainedwithout the presence of a recording medium, in contrast to thatdisplayed in FIG. 10. The two-photon excited photoluminescence (TPPL) isproportional to E⁴. FIG. 11 shows the response of electric field (E⁴) asa function of peg height (in nm) for pegs having various widths (30 nm,40 nm, 45 nm, and 60 nm). A suitable peg height can be around 35 nm to38 nm and NFT response only varies slightly as a function of peg width.However, the value of peg height modeled without media is shifted about10 nm-15 nm from the modeled result shown in FIG. 10 with media present.Additionally, it has been found that the optimal peg height is onlyslightly affected by the diameter of the enlarged disk area of lollipopNFTs.

FIG. 12 is a plot of recording performance (measured in signal-to-noiseratio) as a function of calculated NFT overlap (related to peg height)for various lots of wafer bars containing NFTs with different pegheights. The calculated NFT overlap was computed using an electricallapping guide when the slider was lapped. There is typically an offsetbetween the actual peg height and the calculated NFT overlap dependingupon the type of wafer, the size of the enlarged disk, and the barlapping. The data presented in FIG. 12 was obtained from NFTs that wereexcited by 830 nm light. FIG. 12 shows that there is a dependence ofsignal-to-noise ratio (S/N) on peg height (NFT overlap). NFT overlap canbe positive, negative or zero. The NFT overlap is zero when the peg hasbeen fully lapped away from the NFT. A positive NFT overlap indicates anoverlapped peg (lapped beyond the peg/enlarged disk break point) so thatthere is no peg present in the NFT. FIGS. 12 and 13 show recordingperformance and TPPL current, respectively, as a function NFT overlapfor NFT overlaps increasing from a negative NFT overlap (peg present) toa positive NFT overlap (no peg present).

FIG. 13 is graph of two-photon photoluminescence (TPPL) signal (nA) as afunction of calculated NFT overlap for exciting the NFT with 830 nmlight with an incident laser power of 150 μW. Shown are different lotsof wafer bars (from the same lot) containing NFTs that have beensubjected to 30 nm slope lapping. On resonance, the signal is greaterthan 100 nA; off resonance the signal is less than about 10 nA. FIG. 13shows that there is a dependency of TPPL current on peg height (NFToverlap). The data in FIG. 12 and FIG. 13 show that TPPL currentnecessarily is also a function of recording performance and that both ofthese parameters are affected by peg height in lollipop NFTs.

FIG. 14 is a plot of TPPL current at resonance vs. peg height (nm). Thepeg height was calibrated using cross-sectional TEM on some of the NFTs.An example of a TEM is shown in FIG. 15. The lollipop NFT in FIG. 15includes enlarged disk region 1505 and peg region 1507. Peg height 1510is determined from the TEM image. The data in FIG. 14 show that a pegheight (e.g., optimum, measured using TPPL which is related to recordingperformance) is from about 20 nm to about 30 nm, from about 18 nm toabout 28 nm, or even about 25 nm. This value may not be affected verymuch by enlarged disk diameter or peg width as discussed above. Asuitable peg height of about 25 nm is for pegs in lollipop NFTs thathave no media present. In the present disclosure, optimum peg heightrefers to a peg height or peg heights that are within 25%, are within10%, are within 5%, are within 2%, or are within 1% of the maximum pegheight (measured using a slope bar, for example) determined by themaximum photoluminescent signal using the characterization methoddescribed above.

Based upon the data presented in FIGS. 10 and 11, there is about a 10-15nm shift (red shift) in the optimum peg height when media is present.Based upon this data, a suitable peg height of a lollipop NFT is fromabout 20 nm to about 30 nm or about 25 nm with no media present andshould be from about 10 nm to about 20 nm or about 15 nm in a HAMR writehead with media present.

FIG. 16 is a flow diagram of a method for characterizing the peg regionof an NFT. Excitation radiation is provided 1610 to one or more NFTsdisposed in one or more sliders. In some implementations, the excitationradiation source may be aligned with a waveguide input coupler of an NFTbefore the characterization of the peg region of the NFT occurs. Theexcitation radiation is configured to excite the NFTs to emitphotoluminescent radiation. Excitation radiation that is not absorbed bythe slider and/or NFT emanates from the air bearing surface (ABS) of theslider along with the photoluminescent radiation. The radiationemanating from the ABS is filtered 1620 using a low pass filter thatsubstantially passes the photoluminescent radiation. The filteredradiation is detected 1630 and the peg region is characterized 1640using the detected radiation.

Some embodiments involve processes used to make sliders having aspecified peg height based on characterization of the peg region usingTPPL techniques as discussed herein. A process for fabrication ofsliders is illustrated by the flow diagram of FIG. 17. A bar of slidershaving multiple NFTs can be slope lapped or otherwise formed so that thebar includes NFTs having a number of different peg heights. In someimplementations, the slope lapping may produce peg heights from 0 to 50nm, or any other convenient range, for example. Excitation radiation isprovided 1710 to an NFT disposed on the slider bar. The excitationradiation is configured to excite the NFTs to emit photoluminescentradiation. Excitation radiation that is not absorbed by the sliderand/or NFT emanates from the air bearing surface (ABS) of the slideralong with the photoluminescent radiation. The radiation emanating fromthe ABS is filtered 1720 using a low pass filter that substantiallypasses the photoluminescent radiation. The filtered TPPL radiation isdetected 1730. The TPPL current produced by the detector is measured1740. If there are more 1750 sliders on the bar to be tested, theprocess 1710-1740 is repeated 1760 for the next NFT until the NFTs havebeen characterized. For example, characterization of number of NFTs ofdiffering heights may produce TPPL measurement data similar in form tothe graph of FIG. 14. A peg height that provides a specified NFTperformance is identified from the measurement data.

The identified peg height may be any peg height that provides NFTperformance within an acceptable performance range. In some scenarios,the identified peg height identified may be the peg height that providesoptimal NFT performance based on the peak value of the measured TPPLcurrent with respect to peg height. In some scenarios, a peg height isidentified from a range of peg heights that provide NFT performance (asindicated by measured TPPL current) within a specified range, e.g.,+/−1%, +/−2%, +/−5%, +/−10 or +/−25% of the optimum NFT performance. Theidentified peg height is used to produce a fabrication guide, e.g.,electric lapping guide, used for lapping slider bars to provide slidershaving NFTs with the identified peg height.

Although specific embodiments have been illustrated and describedherein, it will be appreciated by those of ordinary skill in the artthat a variety of alternate and/or equivalent implementations can besubstituted for the specific embodiments shown and described withoutdeparting from the scope of the present disclosure. This application isintended to cover any adaptations or variations of the specificembodiments discussed herein. Therefore, it is intended that thisdisclosure be limited only by the claims and the equivalents thereof.

What is claimed is:
 1. A write head for a heat-assisted magneticrecording medium, comprising: a near-field transducer comprising anenlarged disk region and a peg region at least partially in contact withthe enlarged region, the peg region having peg height from about 15 nmto about 30 nm.
 2. The write head of claim 1, wherein the peg region hasa peg height of from about 18 nm to about 28 nm.
 3. The write head ofclaim 1, wherein the peg region has a peg height of about 25 nm.
 4. Thewrite head of claim 1, wherein the enlarged disk region has a diameterof about 250 nm.
 5. The write head of claim 1, wherein the near-fieldtransducer is configured for an excitation wavelength of 830 nm.
 6. Thewrite head of claim 1, further comprising a waveguide that deliverslight from a light source to the near-field transducer.
 7. The writehead of claim 6, further comprising a solid immersion mirror thatfocuses light from the waveguide onto the near-field transducer.
 8. Thewrite head of claim 6, wherein the waveguide comprises a straight pathfrom the light source to the near-field transducer.
 9. The write head ofclaim 1, wherein the near-field transducer is formed of gold.
 10. Awrite head for a heat-assisted magnetic recording medium, comprising: alight source; a waveguide optically coupled to the light source; and anear-field transducer coupled to the waveguide, the near-fieldtransducer comprising an enlarged disk region and a peg region at leastpartially in contact with the enlarged region, the peg region having pegheight from about 15 nm to about 30 nm.
 11. The write head of claim 10,wherein the peg region has a peg height of from about 18 nm to about 28nm.
 12. The write head of claim 10, wherein the peg region has a pegheight of about 25 nm.
 13. The write head of claim 10, wherein theenlarged disk region has a diameter of about 250 nm.
 14. The write headof claim 10, wherein the near-field transducer is configured for anexcitation wavelength of 830 nm.
 15. The write head of claim 10, furthercomprising a solid immersion mirror that focuses light from thewaveguide onto the near-field transducer.
 16. The write head of claim10, wherein the waveguide comprises a straight path from the lightsource to the near-field transducer.
 17. The write head of claim 10,wherein the near-field transducer is formed of gold.
 18. A write headfor a heat-assisted magnetic recording medium, comprising: a near-fieldtransducer comprising: means for receiving light and resonating at anexcitation frequency; and a peg region having peg height from about 15nm to about 30 nm and configured to receive energy resulting from theresonating at the excitation frequency and transfer the energy to arecording medium.
 19. The write head of claim 18, further comprisingmeans for directing the light onto the means for receiving the light.20. The write head of claim 19, further comprising means for generatingthe light, the light being received by the means for directing thelight.